Nanowire battery

A nanowire battery uses nanowires to increase the surface area of one or both of its electrodes. Some designs(Silicon, Germanium and Transition metal oxides), variations of the lithium-ion battery have been announced, although none are commercially available. All of the concepts replace the traditional graphite anode and could potentially improve battery performance.


  • Silicon 1
  • Germanium 2
  • Transition Metal Oxides(TMO) 3
    • Lead oxide anode(PbO2) 3.1
    • Manganese oxide(MnO2) 3.2
    • Heterostructure TMOs 3.3
  • See also 4
  • References 5
  • External links 6


Silicon is a desirable material for lithium battery anodes because it offers extremely desirable material properties. Silicon has a low discharge potential and a high theoretical charge capacity ten times higher than that of typical graphite anodes currently used in industry. Nanowires could improve these properties by increasing the amount of available surface area in contact with the electrolyte, thereby increasing the anode’s power density and allowing for faster charging and higher current delivery. However, the use of silicon anodes in batteries have been limited by the volume expansion during lithiation. Silicon swells by 400% as it intercalates lithium during charging, resulting in degradation of the material. This volume expansion occurs anisotropically, caused by crack propagation immediately following a moving lithiation front. These cracks result in pulverization and substantial capacity loss noticeable within the first few cycles.[1]

Research done at Stanford University indicates that silicon nanowires grown directly on the current collector (via VLS growth methods) are able to circumvent the negative effects associated with volume expansion. This geometry lends itself to several advantages. First, the nanowire diameter allows for improved accommodation of volume changes during lithiation without fracture. Second, each nanowire is attached to the current collector such that each can contribute to the overall capacity. Third, the nanowires are direct pathways for charge transport; in particle-based electrodes, charges are forced to navigate interparticle contact areas (a less efficient process). Silicon nanowires have a theoretical capacity of roughly 4,200 mAh g^-1, which is larger than the capacity of other forms of silicon. This value indicates a significant improvement over graphite, which has a theoretical capacity of 372 mAh g^-1.[2]

Additional research has involved depositing a carbon coating onto the silicon nanowires, which helps stabilize the material such that a stable solid electrolyte interphase (SEI) forms. An SEI is an inevitable byproduct of the electrochemistry that occurs in the battery; its formation contributes to decreased capacity in the battery since it is an electrically insulating phase (despite being ionically conductive). It can also dissolve and reform over multiple battery cycles.[3] Hence, a stable SEI is preferable in order to prevent continued capacity loss as the battery is used. When carbon is coated onto silicon nanowires, capacity retention has been observed at 89% of the initial capacity after 200 cycles. This capacity retention is on par with that of graphitic anodes today.[4]

One design uses a stainless steel anode covered in silicon nanowires. Silicon stores ten times more lithium than graphite, offering increased energy density. The large surface area increases the anode's power density, allowing for fast charging and high current delivery. The anode was invented at Stanford University in 2007.

In September 2010, researchers demonstrated 250 charge cycles maintaining above 80 percent of initial storage capacity.[5] However, some studies pointed out that Si nanowire anodes shows significant fade in energy capacity with more charge cycles caused by the volumetric expansion of Si nanowires during nanotube with silicon oxide ion-permeating layer as coating.[7]

The silicon nanowire-based battery cell also provides opportunity for dimensional flexible energy source, which would also leads to the development of wearable technological device. Scientist from Rice University showed this possibility by depositing porous copper nanoshells around the silicon nanowire within a polymer matrix. This lithium-polymer silicon nanowire battery (LIOPSIL) has a sufficient operational full cell voltage of 3.4V and is mechanically flexible and scalable.[8]

Commercialization was originally expected to occur in 2012,[9] but was later deferred to 2014.[10] A related company, Amprius, shipped a related device with silicon and other materials in 2013.[10] Canonical announced on July 22, 2013, that its Ubuntu Edge smartphone would contain a silicon-anode lithium-ion battery.[11]

In January 2015, EaglePicher announced that it has signed an engineering agreement and a license agreement with OneD Material, a spin-out from Nanosys, to vertically integrate the production of a "silicon nanowire on graphite" anode called SiNANOde(tm) into new high energy density cells and batteries manufactured in Joplin, MO.[12]


An anode using germanium nanowire was claimed to have the ability to increase the energy density and cycle durability of lithium-ion batteries. Like silicon, germanium has a high theoretical capacity (1600 mAh g-1), expands during charging, and disintegrates after a small number of cycles.[13][14] However, germanium is 400 times more effective at intercalating lithium than silicon, making it an attractive anode material. The anodes claimed to retain capacities of 900 mAh/g after 1100 cycles, even at discharge rates of 20–100C. This performance was attributed to a restructuring of the nanowires that occurs within the first 100 cycles to form a mechanically robust, continuously porous network. Once formed, the restructured anode loses only 0.01% of capacity per cycle thereafter.[15] The material forms a stable structure after these initial cycles that is capable of withstanding pulverization. In 2014, researchers at Missouri University of Science and Technology developed a simple way to produce nanowires of germanium from an aqueous solution.[16]

Transition Metal Oxides(TMO)

Transition metal oxides(TMO), such as Cr2O3, Fe2O3, MnO2, Co3O4 and PbO2, have many advantages as anode materials over conventional cell materials for Lithium-ion battery(LIB) and other battery systems.[17][18][19] Some of them possess high theoretical energy capacity, and are naturally abundant, non-toxic and also environmental friendly. As the concept of the nanostructred battery electrode has been introduced, experimentalists start to look into the possibility of TMO-based nanowires as electrode materials. Some recent investigations into this concept are discussed in the following subsection.

Lead oxide anode(PbO2)

Lead-acid battery is the oldest type of rechargeable battery cell. Even though the raw material (PbO2) for the cell production is fairly accessible and cheap, lead-acid battery cells have relatively small specific energy.[20] The paste thickening effect(volumetric expansion effect) during the operation cycle also blocks the effective flow of the electrolyte. These problems limited the potential of the cell to accomplish some energy-intensive tasks.

In 2014, experimentalist successfully obtained PbO2 nanowire through simple template electrodeposition. The performance of this nanowire as anode for lead-acid battery has also been evaluated. Due to largely increased surface area, this cell was able to deliver an almost constant capacity of about 190 mAh g−1 even after 1,000 cycles.[21][22] This result showed this nanostructured PbO2 as a fairly promising substitute for the normal lead-acid anode.

Manganese oxide(MnO2)

MnO2 has always been a good candidate for electrode materials due to its high energy capacity, non-toxicity and cost effectiveness. However, lithium-ion insertion into the crystal matrix during charging/discharging cycle would cause significant volumetric expansion. To counteract this effect during operation cycle, scientists recently proposed the idea of producing a Li-enriched MnO2 nanowire with a nominal stoichiometry of Li2MnO3 as anode materials for LIB. This new proposed anode materials enable the battery cell to reach an energy capacity of 1279 mAh g−1 at current density of 500 mA even after 500 cycles.[23] This performance is much higher than that of pure MnO2 anode or MnO2 nanowire anode cells.

Heterostructure TMOs

Heterojunction of different transition metal oxides would sometimes provide the potential of a more well-rounded performance of LIBs.

In 2013, researchers has successfully synthesize a branched Co3O4/Fe2O3 nanowire heterostructure using hydrothermal method. This heterojunction can be used as an alternative anode for the LIB cell. At operation, Co3O4 promotes a more efficient ionic transport, while Fe2O3 enhances the theoretical capacity of the cell by increasing the surface area. A high reversible capacity of 980 mAh g−1 was reported.[24]

The possibility of fabrication heterogeneous ZnCo2O4/NiO nanowire arrays anode has also been explored in some studies.[25] However, the efficiency of this material as anode is still to be evaluated.

See also


  1. ^
  2. ^
  3. ^
  4. ^
  5. ^
  6. ^
  7. ^
  8. ^
  9. ^
  10. ^ a b
  11. ^
  12. ^
  13. ^
  14. ^
  15. ^
  16. ^ Simpler process to grow germanium nanowires could improve lithium-ion batteries, Missouri S&T, 28 August 2014, Andrew Careaga
  17. ^
  18. ^
  19. ^
  20. ^
  21. ^
  22. ^
  23. ^
  24. ^
  25. ^

External links

  • Graphene-Silicon Anodes for Li-ion Batteries Go Commercial.
  • XGS presents new silicon-graphene anode materials for lithium-ion batteries.
This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.

Copyright © World Library Foundation. All rights reserved. eBooks from Project Gutenberg are sponsored by the World Library Foundation,
a 501c(4) Member's Support Non-Profit Organization, and is NOT affiliated with any governmental agency or department.