Wire bonding

Article Id: WHEBN0000230283
Reproduction Date:

Title: Wire bonding  
Author: World Heritage Encyclopedia
Language: English
Subject: Microfabrication, Power MOSFET, Flip chip, Wafer bonding, Microtechnology
Collection: Articles Containing Video Clips, Packaging (Microfabrication), Semiconductor Device Fabrication
Publisher: World Heritage Encyclopedia
Publication
Date:
 

Wire bonding

Gold wire ball-bonded to a gold contact pad
Aluminium wires wedge-bonded to a KSY34 transistor die
Germanium diode AAZ15 bonded with gold wire.
The interconnections in a power package are made using thick (250 to 400 µm), wedge-bonded, aluminium wires.

Wire bonding is the method of making interconnections between an integrated circuit (IC) or other semiconductor device and its packaging during semiconductor device fabrication. Although less common, wire bonding can be used to connect an IC to other electronics or to connect from one PCB to another. Wire bonding is generally considered the most cost-effective and flexible interconnect technology, and is used to assemble the vast majority of semiconductor packages. If properly designed, wire bonding can be used at frequencies above 100 GHz.[1]

Contents

  • Materials 1
  • Attachment techniques 2
  • See also 3
  • References 4

Materials

Bondwires usually consist of one of the following materials:

Wire diameters start at 15 µm and can be up to several hundred micrometres for high-powered applications.

The wire bonding industry is transitioning from gold to copper.[2][3] This change has been instigated by the rising cost of gold and the comparatively stable, and much lower, cost of copper. While possessing higher thermal and electrical conductivity than gold, copper had previously been seen as less reliable due to its hardness and susceptibility to corrosion. By 2015, it is expected that more than a third of all wire bonding machines in use will be set up for copper.[4]

Copper wire has become one of the preferred materials for wire bonding interconnects in many semiconductor and microelectronic applications. Copper is used for fine wire ball bonding in sizes up to 0.003 inch (75 micrometres). Copper wire has the ability of being used at smaller diameters providing the same performance as gold without the high material cost.[5]

Copper wire up to 0.010 inch (250 micrometres) can be successfully wedge bonded with the proper set-up parameters. Large diameter copper wire can and does replace aluminum wire where high current carrying capacity is needed or where there are problems with complex geometry. Annealing and process steps used by manufacturers enhance the ability to use large diameter copper wire to wedge bond to silicon without damage occurring to the die.[5]

Copper wire does pose some challenges in that it is harder than both gold and aluminum, so bonding parameters must be kept under tight control. The formation of oxides is inherent with this material, so storage and shelf life are issues that must be considered. Special packaging is required in order to protect copper wire and achieve a longer shelf life.[5] Palladium coated copper wire is a common alternative which has shown significant resistance to corrosion, albeit at a higher hardness than pure copper and a greater price, though still less than gold. During the fabrication of wire bonds, copper wire, as well as its plated varieties, must be worked in the presence of forming gas [95% nitrogen and 5% hydrogen] or a similar anoxic gas in order to prevent corrosion. A method for coping with copper's relative hardness is the use of high purity [5N+] varieties.[4]

Red, Green, Blue surface mount LED package with gold wire bonding details.

Pure gold wire doped with controlled amounts of beryllium and other elements is normally used for ball bonding. This process brings together the two materials that are to be bonded using heat, pressure and ultrasonic energy referred to as thermosonic bonding. The most common approach in thermosonic bonding is to ball-bond to the chip, then stitch-bond to the substrate. Very tight controls during processing enhance looping characteristics and eliminate sagging.

Junction size, bond strength and conductivity requirements typically determine the most suitable wire size for a specific wire bonding application. Typical manufacturers make gold wire in diameters from 0.0005 inch (12.5 micrometres) and larger. Production tolerance on gold wire diameter is +/-3%.[6]

Alloyed aluminum wires are generally preferred to pure aluminum wire except in high-current devices because of greater drawing ease to fine sizes and higher pull-test strengths in finished devices. Pure aluminum and 0.5% magnesium-aluminum are most commonly used in sizes larger than 0.004 inch.

All-aluminum systems in semiconductor fabrication eliminate the "purple plague" (brittle gold-aluminum intermetallic compound) sometimes associated with pure gold bonding wire. Aluminum is particularly suitable for thermosonic bonding.

In order to assure that high quality bonds can be obtained at high production speeds, special controls are used in the manufacture of 1% silicon-aluminum wire. One of the most important characteristics of high grade bonding wire of this type is homogeneity of the alloy system. Homogeneity is given special attention during the manufacturing process. Microscopic checks of the alloy structure of finished lots of 1% silicon-aluminum wire are performed routinely. Processing also is carried out under conditions which yield the ultimate in surface cleanliness and smooth finish and permits entirely snag-free de-reeling.[7]

Attachment techniques

Demonstration of ultrasonic wedge bonding of an aluminium wire between gold electrodes on a PCB board and gold electrodes on a sapphire substrate, reverse bonding order.

The main classes of wire bonding:

Ball bonding usually is restricted to gold and copper wire and usually requires heat. Wedge bonding can use either gold or aluminum wire, with only the gold wire requiring heat.

In either type of wire bonding, the wire is attached at both ends using some combination of heat, pressure, and ultrasonic energy to make a weld.

Compliant bonding[8] transmits heat and pressure through a compliant or indentable aluminum tape and therefore is applicable in bonding gold wires and the Beam leads that have been electroformed to the silicon integrated circuit (known as the Beam leaded integrated circuit).

See also

References

  1. ^ V. Valenta et al., "Design and experimental evaluation of compensated bondwire interconnects above 100 GHz, International Journal of Microwave and Wireless Technologies, 2015
  2. ^ Mokhoff, Nicolas (March 26, 2012). "Red Micro Wire encapsulates wire bonding in glass".  
  3. ^ "Product Change Notification - CYER-27BVXY633". microchip.com. August 29, 2013. Archived from the original on March 20, 2014. Retrieved March 20, 2014. 
  4. ^ a b Chauhan, Preeti; Choubey, Anupam; Zhong, ZhaoWei; Pecht, Michael (2014). Copper Wire Bonding (PDF).  
  5. ^ a b c "Copper Bonding Wire: Electrical Interconnect Materials". coininginc.com. March 20, 2014. Archived from the original on March 20, 2014. Retrieved March 20, 2014. 
  6. ^ "Gold Bonding Wire and Ribbon: Wire for Automatic Bonders". coininginc.com. March 20, 2014. Archived from the original on March 20, 2014. Retrieved March 20, 2014. 
  7. ^ "Aluminum Bonding Wire and Ribbon: Silicon Aluminum Wire, Aluminum Ribbon". coininginc.com. March 20, 2014. Archived from the original on March 20, 2014. Retrieved March 20, 2014. 
  8. ^ A.Coucoulas, “Compliant Bonding” Proceedings 1970 IEEE 20th Electronic Components Conference, pp. 380-89, 1970. https://www.researchgate.net/publication/225284187_Compliant_Bonding_Alexander_Coucoulas_1970_Proceeding_Electronic_Components_Conference_Awarded_Best_Paper
  • Copper (Cu) Wire Bonding

Challenging the limits of bonding wire

This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and USA.gov, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for USA.gov and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
 
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
 
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.
 


Copyright © World Library Foundation. All rights reserved. eBooks from Project Gutenberg are sponsored by the World Library Foundation,
a 501c(4) Member's Support Non-Profit Organization, and is NOT affiliated with any governmental agency or department.