Coin Die

In minting, coining or coinage is the process of manufacturing coins using a kind of stamping which is now generically known in metalworking as "coining". This process is different from cast coinage, and can be classified in hammered coinage or hammering and milled coinage or milling.

A coin die is one of the two metallic pieces that are used to strike one side of a coin. A die contains an inverse version of the image to be struck on the coin.

Modern dies made out of hardened steel are capable of producing many hundreds of thousands of coins before they are retired and defaced.

Ancient coin dies

Prior to the modern era, coin dies were manufactured individually by hand by artisans known as engravers. In demanding times, such as the crisis of the Roman Empire in the 3rd century, dies were still used even when they became very worn or even when they cracked. The die that was on the hammer side, usually the reverse (back),[1] tended to wear out first.[2] The flans were usually hot prior to striking.[2] On some Roman provincial coins, some believe the tongs used to move the heated flan left permanent center indentations on the finished coins. Others attribute these marks to surfacing tools used as a part of flan preparation.

Medieval coin dies

Medieval engravers were guild members who created coins in mints.

The vast majority of medieval coins were cold struck; the planchets were not heated. While medieval coin dies were largely made of iron, some dies have been discovered with a small region at the face of the die which is made of steel. As technology and the economy changed over the course of the Middle Ages, so did the techniques used to create coin dies. While most ancient coin dies used engraving very heavily, early medieval coinage was dominated by dies created mostly from punches, which displace the metal of the die instead of removing it. There is evidence of medieval die cutters using engraving tools to lay out designs, and to create detailed punches. However, engraving on the face of the die did not become commonplace until the early Renaissance.

Very detailed records exist for the Venetian mint. In the late Middle Ages, the dies used to create tornesellos lasted as follows: "hammer" die, ~17,000 strikes; "anvil" die, 36,000 strikes. The mint made an average of 20,000 coins per day, so they were making one hammer die a day and one anvil die every other day. The "hammer" dies wore out quicker because they tended to be smaller and were hit directly with a hammer, leading to severe mushrooming on the tops.

Modern die production

First, an artist creates a large plaster model of the coin. The plaster model is then coated with rubber. The rubber mold is then used to make an epoxy galvano. All of this takes place on a scale of around eight inches. Next, a Janvier reducing lathe takes several days to reduce the image onto a steel master hub. The master hub is then heat treated to make it hard. The master hub is then used to make only a few master dies via hubbing, which involves pressing the master hub into a steel blank to impress the image into the die. The master die is then used to form as many working hubs as needed through the same process, and then the working hubs are put through the same process to form the working dies. These working dies are the actual dies which will strike coins. The process of transferring the hub to the die can be repeated as many times as necessary in order to form the number of dies needed to make the amount of coins required. The difference between a hub and a die is that the hub has a raised image and a die has an incuse image, so one forms the other.

When making working dies, the Mint has found that by using a lower amount of pressure in the hubbing press, they can prolong the life of the hubs and dies used. In between each hubbing, however, the die being made must be subjected to an annealing procedure to soften the steel, making it easier to force the hub's image into the die. As the die is being cold forged in the hubbing press, the die's steel work hardens making the hubbed die harder and stronger than in its original state (an advantage over engraving the die).

If, when the die is subjected to another hubbing, it is not lined up exactly with the hub, the result is a secondary image, or doubling. This is called die doubling, and results in such spectacular coins as the famous 1955 doubled die cent.

The third side of the coin

On the edge of the US dime, quarter and half dollar, and many world coins there are ridges, similar to knurling, called reeds. Some older US coins, and many world coins have other designs on the edge of the coin. Sometimes these are simple designs like vines, more complex bar patterns or perhaps a phrase, as on the United States dollar coin, on which are the date, mintmark, and motto, E Pluribus Unum. Historically these kinds of designs are imparted into the coin through a multisectioned third die called a collar, whose inner edge diameter is the same as that of the edge of the coin. When the obverse and reverse dies strike the planchet the planchet expands to fill the collar, impressing the collar design into the edge of the coin. The collar sections are then separated to allow the coin to be removed. When the collar is missing, it results in a type of error called a broadstrike. A broadstruck coin is generally a bit flatter and quite a bit bigger around than the regular non-error coin of the same denomination. A second and faster process by which a design is applied to the edge of a coin is by use of an edge incusing machine. The struck coin is feed into the machine and the machine then pressed the design into the edge of the coin. Sometimes a mint will use both methods to apply an edge design. The U.S. Mint, for example, used an edge incusing machine to letter the edges business strike presidential dollars and a collar for the proof versions of these coins.

Die Marriage

During a typical production run, or coining process, (particularly when heavy presses are used for large production runs) a die is selected for the front and another die is selected for the back of the coin to be made. In some cases, there is more than one die (front and/or back) from which to select. The mint employee then places each die into the minting press for operation. When the run is complete, the dies are removed from the press. This procedure is repeated for each production run. Coins minted by each mint for each year may have several production runs in order to complete their orders.

If there is more than one die used for either the front or the back, then minute differences between each die can be identified. In addition, the relative positioning between the back and the front can also be used to determine which dies were used for the run that produced a particular coin. In the United States, coins are typically minted head to tail; that means the "top" of one side of the coin is on the exact opposite side of the coin as the "bottom" of the other, resulting in the coin's features being presented right side up when the coin is turned on a horizontal axis. This is called a "coin turn" alignment. Correct alignment for a "coin turn" is exactly 180 degrees; however due to realities of machine process, this can vary by a fraction of a degree. In rare cases, this deviation can be up to several degrees, and very easily noticeable. However, even very small deviations can establish the production run in which a coin was minted. When this is done, it is called a die marriage. Die marriage is particularly important with regards to the US half dollar minted at the New Orleans Mint in 1861, since it establishes if a coin was minted with the mint facility under Union, State of Louisiana, and Confederacy control.


In modern presses, a die strikes approximately 120 coins a minute. This rapid coining causes wear on the dies. Nickel alloys are among the main metals used in today’s coins but they are harder than other legacy coinage metals such as silver and gold alloys and therefore they cause even quicker die wear. Copper and copper alloys have been used in coinage for centuries because of their malleability and the ease with which they can be coined: however, these too wear the dies when the dies are used for too long. An infamous example is the 1955 "poorman’s double die." This coin is sold as a replacement for the 1955 doubled die, but it is no more than Die Deterioration Doubling, caused by wear on the dies. When a coin is struck, the planchet is not heated. Although the planchet would be softer and more malleable, the extra time and expense would prove too great for the mint. Thus, the metal cold flows into the die under the high pressure.

Mistakes can happen at any stage of this manufacturing process, and these mistakes are something that certain collectors look for. Coin errors that occur on the die are generally more desirable than errors made at the time of the strike. For example, a doubled die, where a date or another device appears twice slightly offset, is often a highly desired error. Strike errors are generally unique, whereas all coins struck with an error die will have the same characteristic. This makes them more easily collectible. The most famous doubled die in the past hundred years is the 1955 doubled die Lincoln cent. These trade for hundreds of dollars because the error can easily be seen by a casual observer. Many doubled die errors require at least a jeweler's loupe to be seen. Doubling can occur at the hub stage as well. Some more recent errors are hub doubled. Most famously, there is a 1995 doubled die cent that is hub doubled.

Terminal Die State

The terminal die state, as the name would seem to indicate, is the last state in which any die is used. This state refers to a die that is starting to develop serious structural failures through cracks. A die in such a state would, if not removed from service, become unserviceable by breaking apart. Like any metallic part, dies are subject to failure from the enormous pressures used to impress the image of the die onto the blank planchet. Some dies were removed when even a microscopic defect is observed, while others were used until they literally broke into pieces. The Bass Foundation has a particularly noteworthy example of an 1806/4 Quarter Eagle ($2.50 gold US coin) in which a piece of the die has broken away, resulting in a heavy rim break over the "LI" in "LIBERTY" on the front. (Source:, HBCC-3014)

More typically, a terminal die state will result in crack-like structures appearing on the coin. A good example can be observed on an 1839 Liberty Seated Dime. A crack-like feature is clearly seen going through the date, the shield, and the second star. (Source:, Major 100 Varieties, number 12 has the most pronounced features) This crack-like structure appears like material that is overlaid onto the surface of the coin; this is because the crack on the die allowed the planchet materiel to flow into it during stamping, just like a deliberate design feature. Some coins exhibit multiple crack-like features, indicating a die that is very close to the end of its serviceable life. Coins that do exhibit such features can be labeled as “Terminal Die State” examples.

Coin die represented in other coins

A coin die itself, has been the main motive for many collectors coins and medals. One of the most recent and famous one, is the Austrian 700 Years City of Hall in Tyrol coin, minted on January 29, 2003. The reverse side of the coin shows the Guldiner silver coin. However, the design is negative, representing a coin die, as a reference to Hall’s history as a significant centre for minting coins.

See also


External links

  • Designing and minting coins The creation of a die and the minting process
  • US Treasury: Preparation of Working Dies
This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.